Austenitic / dissimilar steel

Product Detail

Standards compliant:GB/T17853 E307LT1-1

AWS A5.22 E307LT1-1


Characteristics and applications:

1.Major component 18%Cr-8%Ni-4%Mn making dissimilar steel welding featuring favorable crack resistance;

2.Featuring stable arc, little spatter, favorable detachability, stable wire feedability, beautiful appearance and other favorable welding performance;

3.Applicable to armor plates, nuclear submarines and other special nonmagnetic requirements and welding of dissimilar steel which may crack easily.


Welding position



Chemical composition (wt%)

Alloy wt% C Mn Si Cr Ni Mo P S Cu
GB/T 0.130 3.3-4.75 1.0 18-20.5 9.0-10.5 0.5-1.5 0.04 0.03 0.50
AWS 0.130 3.3-4.75 1.0 18-20.5 9.0-10.5 0.5-1.5 0.04 0.03 0.75
Case value 0.024 3.81 0.55 19.60 9.5 0.8 0.015 0.003 0.015


Mechanical properties

Mechanical properties

Yield strength MPa

Tensile strength MPa 


Impact valueJ /°C

GB/T - 590 30 -
AWS - 590 30 -
Case value - 615 39 -


Recommended current range: (DC+)

Diameter of welding wire (mm) 1.2 1.6

Voltage (V)

22-36 26-38

Current (A)

120-260 200-300

Extension length (mm)

15-20 18-25

Gas flow (l/min)

15-25 15-25


Welding precautions

1.Using CO2 shielding gas with purity ≥99.98% and gas flow of 20-25L/min.

2.Interpass temperature: 16~100°C.

3.During welding, please keep off wind to prevent welding defects caused by flying off shielding gas. Greasy dirt, water, etc. at welding parts shall be removed.

4.Welding wire shall be used up as quickly as possible after unpacking. Moisture-proof measures shall be adopted for those not used up.